TPE/HTR8171/美国杜邦 物性表
规格用途
| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
技术参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 24小时吸水率 | ASTM D-570 | 54 | % | |
| 物理性能 | 熔融指数 | ASTM D-1238 | 9.0 | g/10min | |
| 比重 | ASTM D-792 | 1.17 | |||
| 泰伯磨耗量 | CS-17轮 | ASTM D-1044 | 85 | mg/1000rev | |
| H 18轮 | ASTM D-1044 | 240 | mg/1000rev | ||
| 机械性能 | 断裂拉伸力 | ASTM D-638 | 10.2 | MPa | |
| 硬度计硬度 | ASTM D-2240 | 32 | |||
| 拉伸力 | 5%伸长 | ASTM D-638 | 1.8 | MPa | |
| 10%伸长 | ASTM D-638 | 2.8 | MPa | ||
| 断裂伸长 | ASTM D-638 | 210 | % | ||
| 埃佐冲击强度 | 23℃ | ASTM D-256 | 不破裂 | J/M | |
| 初耐撕裂性能 | ASTM D-1004 | 45 | kn/m | ||
| 揉曲模量 | 23°C | ASTM D-790 | 24.8 | MPa | |
| 热性能 | 热畸变温度 | @0.5Mpa | ASTM D-648 | 42 | ℃ |
| @0.18Mpa | ASTM D-648 | N/A | ℃ | ||
| 熔点 | ASTM D-3418 | 150 | ℃ | ||
| 维卡软化点 | ASTM D-1525 | 76 | ℃ | ||
| 其它性能 | 耐揉曲切口增长性能 | ASTM D-1052 | >1×10 | ||